紀要論文 Thermal Radiative Characteristics of Nanostructured Tungsten at High-Temperature
ナノ構造表面を持つタングステンの高温での熱放射特性の向上
ナノ コウゾウ ヒョウメン オ モツ タングステン ノ コウオン デノ ネツ ホウシャ トクセイ ノ コウジョウ

髙村, 秀一  ,  上杉, 喜彦  ,  菊池, 祐介  ,  永田, 正義  ,  山田, 耕平  ,  小林, 孝裕  ,  前中, 志郎  ,  藤田, 和宣  ,  栗下, 裕明

(52)  , pp.62 - 67 , 2017-03-31 , 愛知工業大学
ISSN:18833217
NII書誌ID(NCID):AA12337561
内容記述
Fiber-form nanostructure grown on tungsten (W) surface has an excellent thermal radiative property at relatively low sample temperature up to 1200℃. Requirement of maintaining the above radiative property at higher temperature promotes an examination on recovery or annealing characteristics of nanostructured W surfaces, making an emphasis on dopant effect. TFGR-W-1.1%TiC/H (Toughing, Fine-Grained Recrystallized Tungsten with TiC dispersoid) was found to have best characteristics among tested doped W. However, it was noted and discussed that a further improvement at higher-temperature needs an additional processes.
本文を読む

http://repository.aitech.ac.jp/dspace/bitstream/11133/3204/1/%e7%b4%80%e8%a6%8152%e5%8f%b7%28p62-p67%29.pdf

このアイテムのアクセス数:  回

その他の情報