学術雑誌論文 Formation and Stability of Interface between Garnet-Type Ta-doped Li7La3Zr2O12 Solid Electrolyte and Lithium Metal Electrode

稲田, 亮史  ,  安田, 哲志  ,  細川, 寛将  ,  斎藤, 正也  ,  東城, 友都  ,  櫻井, 庸司

4 ( 2 )  , p.26 , 2018-06-07 , MDPI
ISSN:2313-0105
内容記述
Garnet-type Li7-xLa3Zr2-xTaxO12 (LLZT) is considered a good candidate for the solid electrolyte in all-solid-state lithium batteries because of its reasonably high conductivity around 10-3 S cm-1 at room temperature and stability against lithium (Li) metal with the lowest redox potential. In this study, we synthesized LLZT with a tantalum (Ta) content of 0.45 via a conventional solid-state reaction process and constructed a Li/LLZT/Li symmetric cell by attaching Li metal foils on the polished top and bottom surfaces of an LLZT pellet. We investigated the influence of heating temperatures and times on the interfacial charge-transfer resistance between LLZT and the Li metal electrode. In addition, the effect of the interface resistance on the stability for Li deposition and dissolution was examined using a galvanostatic cycling test. The lowest interfacial resistance of 25 ohm cm2 at room temperature was obtained by heating at 175 degree Celsius (5 degree Celsius lower than the melting point of Li) for three to five hours. We confirmed that the current density at which the short circuit occurs in the Li/LLZT/Li cell via the propagation of Li dendrite into LLZT increases with decreasing interfacial charge transfer resistance.
本文を読む

https://repo.lib.tut.ac.jp/?action=repository_action_common_download&item_id=2049&item_no=1&attribute_id=22&file_no=1

このアイテムのアクセス数:  回

その他の情報