会議発表論文 酸化チタンとチタンアパタイトの紫外線照射下での表面摩擦力変化

鶴岡, あゆみ  ,  Tsuruoka, Ayumi  ,  磯部, 敏宏  ,  Isobe, Toshihiro  ,  松下, 祥子  ,  Matsushita, Sachiko  ,  中島, 章  ,  Nakajima, Akira

2015-09
内容記述
Photocatalytic activity and surface friction variation were evaluated on Ti-doped hydroxyapatite (Ti-HAp) and anatase-type TiO2 powders under UV illumination. Although the adsorption capability of Ti-HAp against gaseous 2-propanol (IPA) was greater than that of anatase, photocatalytic decomposition activity and water adsorption capability of Ti-HAp under UV illumination were inferior to those of anatase. Experiments using powder/epoxy composites revealed that Ti-HAp didn’t exhibit photo-induced hydrophilicity. The surface friction force variation of anatase under UV illumination was similar to previously reported trend for rutile ceramics. That of Ti-HAp exhibited a different trend, suggesting that its surface was originally more hydrophobic than anatase.
有機物の吸着性に優れる光触媒チタンアパタイトは、光誘起親水性を示さないという報告がなされている。これは、表面エネルギーが元々低いため、または水との競争吸着で有機物の吸着が優勢になるため、ということが考えられる。そこで、紫外線照射下、雰囲気制御により表面摩擦力を測定することで、表面状態を酸化チタンと比較したところ、チタンアパタイトは酸化チタンよりも、親水性であるカンチレバーとの相互作用が小さく、表面エネルギーが元々低いということが示唆された。

このアイテムのアクセス数:  回

その他の情報