Journal Article 円周切欠きを有する丸棒試験片におけるひずみ速度集中係数の提案と応力集中係数の関係についての考察

野田, 尚昭  ,  赤木, 大地  ,  沈, 雨濃  ,  高木, 怜  ,  池田, 朋弘  ,  佐野, 義一  ,  高瀬, 康

83 ( 851 )  , p.17-00034 , 2017-07-25 , 一般社団法人日本機械学会
High-speed tensile testing is now being recognized as a standard testing method for evaluating the impact strength of engineering materials. The impact speeds of Izod and Charpy tests cannot be controlled and therefore do not correspond to the real failure of real products. The brittle-ductile transition of structural materials is affected by the temperature and loading speed. In the high-speed tensile test, it is necessary to obtain the strain rate at the notch root accurately to understand the effect of impact load. For smooth specimens, the strain rate can be determined from the tensile speed u/t and specimen length l as εsmooth = u/tl. For notched specimens, however, the strain rate at the notch root εnotch should be analyzed accurately. In this study, therefore, the strain rate concentration factor defined as Ktε = εnotch/εsmooth is studied with varying the notch geometry. To predict the strain rate concentration factor Ktε accurately, the relationship between Ktε and the stress concentration factor Kt* = σmax/σgross is investigated. Here, σgross is the remote tensile stress and P is the tensile load. It is found that the strain concentration factor Ktε can be estimeted from stress concentration factor Kt* when the relative notch depth 2t/D≦0.5 (t : notch depth, D : the specimen diameter).

Number of accesses :  

Other information