Journal Article Convenient Debonding Strength Evaluation for Spray Coating Based on Intensity of Singular Stress

Noda, Nao-Aki  ,  Uchikoba, Takumi  ,  Ueno, Masayasu  ,  Sano, Yoshikazu  ,  IIda, Kazuki  ,  Wang, Zefeng  ,  Wang, Guohui

55 ( 12 )  , pp.2624 - 2630 , 2015-12-01 , 社団法人日本鉄鋼協会
Hearth rolls are used in continuous annealing furnace to produce thin steel sheet. The roll surface is usually coated by using thermal spraying, which has high adhesive strength and wears resistance. However, in the ceramics coating, thermal stress caused during heating and cooling process in the furnace may lead to debonding due to the low toughness of ceramics. In order to improve the heat resistance of the thermally sprayed coating, it is essential to evaluate the debonding strength. Generally, heat resistance of thermal spray coating is evaluated by thermal shock test prescribed by JIS H8304 although few research is available in terms of singular stress at the end of the interface for JIS specimen under thermal shock. This paper focuses on the intensity of the singular stress at the end of interface. Then, the most suitable conditions are discussed with varying the coating material and the coating thickness.

Number of accesses :  

Other information