学術雑誌論文 Structural transitions in Pb(In1∕2 Nb1∕2 )O3 under pressure

Ahart, Muhtar  ,  Somayazulu, Maddury  ,  Kojima, Seiji  ,  Yasuda, Naohiko  ,  Prosandeev, Sergey  ,  Hemley, Russell J.

05 ( 04 )  , p.1550033 , 2015-12 , World Scientific Publishing
ISSN:2010-135x
内容記述
Room-temperature Raman scattering and x-ray diffraction measurements together with first-principles calculations were employedto investigate the behavior of disordered Pb(In1=2Nb1=2ÞO3 (PIN) under pressure up to 50 GPa. Raman spectra show broad bands buta peak near the 380 cm−1 increases its intensity with pressure. The linewidth of the band at 550 cm−1 also increases with pressure,while two of the Raman peaks merge above 6 GPa. Above 16 GPa, we observe additional splitting of the band at 50 cm−1. Thepressure evolution of the diffraction patterns for PIN shows obvious Bragg peaks splitting above 16 GPa; consistent with asymmetry lowering transition. The transition at 0.5 GPa is identified as a pseudo-cubic to orthorhombic (Pbam) structural changewhereas the transition at 16 GPa is isostructure and associated with changes in linear compressibility and octahedral titling, and thetransition at 30 GPa is associated to an orthorhombic to monoclinic change. First-principles calculations indicate that the Pbamstructure is ground state with antiferrodisdortion consistent with experiment.
本文を読む

https://tsukuba.repo.nii.ac.jp/?action=repository_action_common_download&item_id=37581&item_no=1&attribute_id=17&file_no=1

このアイテムのアクセス数:  回

その他の情報