学位論文 An approach for preparing a bio-hybrid material with special water affinity from poly (vinyl alcohol), rice starch and silk fibroin for wound dressing application

Kuchaiyaphum, Pusita

pp.1 - 65 , 2015-03-23 , 新潟大学
内容記述
学位の種類: 博士(工学). 報告番号: 甲第4043号. 学位記番号: 新大院博(工)甲第425号. 学位授与年月日: 平成27年3月23日
A hybrid material composing of polyvinyl alcohol (PVA), rice starch (RS) and silk fibroin (SF) with opposite water affinity on each surface was successfully prepared. The hybrid material was prepared by placing PVA/RS/SF hydrogel onto glycerolmodified PVA/RS/SF film and leaving them to adhere. SF content in the hydrogels was optimized first by mixing various SF amounts to a mixture of PVA:RS (2:1 by weight). The 8.00 part per hundred of polymer (php) of SF was an appropriate concentration revealed by the maximum values of gel fraction and percent porosity. This SF content caused the blend to exhibit the highest water saturation and best mechanical properties. The glycerol-modified hydrophobic film with the same PVA/RS/SF composition was prepared and found that the water contact angle of the film had increased approximately three times after water soaking. The hybrid material was then prepared and characterized. As evidenced by physical appearance and SEM images, the interfaces between layers became homogeneous after 30 h layering time. Water contact angle values pointed out the hydrophilic nature of the hydrogel surface, while the film surface was hydrophobic. Coupling of the hydrogel with the film improved overall mechanical properties as indicated by stress and % elongation at break.
本文を読む

http://dspace.lib.niigata-u.ac.jp/dspace/bitstream/10191/32206/1/h26ftk425_a.pdf

http://dspace.lib.niigata-u.ac.jp/dspace/bitstream/10191/32206/2/h26ftk425.pdf

このアイテムのアクセス数:  回

その他の情報